Description:
This is a multifunction gun grade polyurethane based construction sealant, it is of high modulus and cures by reaction with atmospheric moisture to form a soft rubber like material with moderate elasticity and high adhesion strength.
Applications:
Features:
Technical Data:
| Item | Range | Typical Data | Typical Data | Typical Data |
| Appearance | Black/White/Grey Homogenous paste |
Black Homogenous paste |
White Homogenous paste |
Grey Homogenous paste |
| Extrudability (ml/min)GB/T13477.4 | ≥80 | 100 | 100 | 100 |
| Sagging Properties (mm) GB/T13477.6 | 0 | 0 | 0 | 0 |
|
Tack free time (min) GB/T 13477.5 |
1~3 | 2 | 2 | 2 |
|
Volatile content (%) GB/T13477.19 |
≤4 | 3 | 3 | 3 |
|
Shore A – hardness GB/T 531.1 |
40~50 | 45 | 45 | 45 |
| Tensile strength (Mpa) GB/T 528 | ≥1.5 | 2.2 | 2.2 | 2.2 |
| Elongation at break (%) GB/T 528 | ≥500 | 600 | 600 | 600 |
|
Tensile modulus (Mpa) GB/T13477.8 23ºC / -20ºC |
≤0.4(60%) / ≤0.6 (60%) | 0.30 / 0.70 | 0.50 / 0.70 | 0.50 / 0.70 |
| Tensile properties at maintained extension GB/T13477.10 | No failure | No failure | No failure | No failure |
| Adhesion/cohesion properties at maintained extension after water immersion GB/T13477.11 | No failure | No failure | No failure | No failure |
| Adhesion/cohesion properties at variable temperature GB/T13477.13 | No failure | No failure | No failure | No failure |
|
Elastic recovery rate (%) GB/T13477.10 |
≥70 | 80 | 80 | 80 |
|
Operating Temperature (ºC): |
-40~90 | |||
Note: All data above were tested under standardized condition
Regular Colors: Black,White, Grey
Packing:
310ml cartridge * 20 or 12pcs/carton
600ml sausage * 20pcs/carton
Shelf Life: 9 months in dry and cool place